Mouldmaking Silicone rubber

產品分類 :

化學->化學原料->合成橡膠

產品規格

Model No:	RTV-2

Country	CN
Brand	COCA
Materials	2.W-DIHYDROXY-POLYDIMETHOXY SILICONE (107#), WHITE CARBON (SIO2) & SILICONE OIL DIBUTYLTIN DILAURATE (DBTD) & TETRAETHYL ORTHOSILICATE (TEOS)
Size	67 x 45.5 x 25 (L x W x H) centimeters
Weight	Gross: 27 Net : 25
Color	Whit, Gray and Transparent
Packing	25 kgs plastic drums
Minimum Order	100 kgs
Payment Term	TT or L/C

產品描述

MOULDMAKING SILICONE RUBBER (AB: RTV-2) IS DOUBLE-COMPONENT SILICONE RUBBER.
COMPONENT A CONTAINS 2.W-DIHYDROXY-POLYDIMETHOXY SILICONE (107#), WHITE CARBON (SIO2) & SILICONE OIL.
COMPONENT B (CATALYST) CONTAINS DIBUTYLTIN DILAURATE (DBTD) & TETRAETHYL ORTHOSILICATE (TEOS).
CURING IN ROOM TEMPERATURE.
CATALYST 3% OR 5% AMOUNT, INTERNATIONAL STANDARD.
A, B & C STYLES CATALYST SUITABLE FOR 10-20, 20-30 & 30-40 RESPECTIVELY.
EXCELLENT PERFORMANCES AS: LOWER SHRINKAGE & DISTORTION RATE, HIGHER TEAR STRENGTH, AND HIGHER
TENSILE STRENGTH & MORE REPEAT USE ETC.
APPLICATION MOULDED FOR:
POLYESTER, EPOXY, POLYURETHANE, LAMP, DECORATIONS MADE OF PU FOAMING, DUPLICATION OF ARTWORKS, ARCHAIZED
FURNITURE, ARTISTIC CANDLES, ARTIFICIAL PLASTIC & RUBBER ETC.;
SHOE MOULD, SOFT SHOE MOULD, SILK SCREEN SHOE MOULD & AFFUSE SHOE MOULD ETC;
GYPSUM & CEMENT MOULD ETC;
JEWELRY & HIGH TEMPERATURE RESISTANCE PRODUCT (LIMIT 300) ETC;
MOVE PRINT RUBBER & SILK PRINT RUBBER;
SPECIAL REGIONAL & GENERAL APPLY.
SPECIAL TECHNOLOGY WILL BE ACCEPTABLE

PL MOULDMAKING SILICONE RUBBER
RTV-2-771
ESPECIALLY APPLIED IN MAKE POLYESTER, EPOXY, POLYURETHANE, LAMP, DECORATIONS
MADE OF PU FOAMING, DUPLICATION OF ARTWORKS, ARCHAIZED FURNITURE, ARTISTIC
CANDLES, ARTIFICIAL PLASTIC & RUBBER ETC. ESPECIAL SUITABLE FOR PL.

COLOUR: WHITE
VISCOSITY: 5-5.5 Mpa.S
CURING TEMP: 25
CURING AMOUNT: 3% or 5%
GEL TIME: 10 Min
CURING TIME: 60 Min HARDNESS: 27 1 JIS A
LIFE-SPAN: 160 TIMES
TEAR STRENGTH: 22 1 N/mm
TENSILE STRENGTH: 32 1 Mpa
ELONGATION RATE: 350%
CATALYST STYLE: 25

PU MOULDMAKING SILICONE RUBBER
RTV-2-334
ESPECIALLY APPLIED IN MAKE POLYESTER, EPOXY, POLYURETHANE, LAMP, DECORATIONS MADE OF PU FOAMING,
DUPLICATION OF ARTWORKS, ARCHAIZED FURNITURE, ARTISTIC CANDLES, ARTIFICIAL PLASTIC & RUBBER ETC.
ESPECIAL SUITABLE FOR PU.

COLOUR: WHITE
VISCOSITY: 5.5 Mpa.S
CURING TEMP: 25
CURING AMOUNT: 3% or 5%
GEL TIME: 10 Min
CURING TIME: 60 Min HARDNESS: 24 JIS A
LIFE-SPAN: 150 TIMES
TEAR STRENGTH: 24 N/mm
TENSILE STRENGTH: 42 Mpa
ELONGATION RATE: 400%
CATALYST STYLE: 25

GYPSUM MOULDMAKING SILICONE RUBBER
RTV-2-830
ESPECIALLY APPLIED IN GYPSUM & CEMENT MOULD ETC.

COLOUR: WHITE
VISCOSITY: 5.3 Mpa.S
CURING TEMP: 25
CURING AMOUNT: 3% or 5%
GEL TIME: 10 Min
CURING TIME: 60 Min HARDNESS: 27 JIS A
LIFE-SPAN: 70 TIMES
TEAR STRENGTH: 22 N/mm
TENSILE STRENGTH: 35 Mpa
ELONGATION RATE: 380%
CATALYST STYLE: 25

JEWELRY MOULDMAKING SILICONE RUBBER
RTV-2-444
FOR HIGH-TEMPERATURE (250-300) PERFORMANCE, ESPECIALLY APPLIED IN HIGH-TEMPERATURE RESISTANCE
PRODUCT MOULD.AS FOR PL, PU, LAMP, CANDLE MOULD ECT. ESPECIAL SUITABLE FOR JEWELRY.LIMIT 300.

COLOUR: WHITE
VISCOSITY: 3.5 Mpa.S
CURING TEMP: 25
CURING AMOUNT: 3% or 5%
GEL TIME: 10 Min
CURING TIME: 60 Min HARDNESS: 50 JIS A
LIFE-SPAN: 120 TIMES
TEAR STRENGTH: 8-10 N/mm
TENSILE STRENGTH: 20 Mpa
ELONGATION RATE: 400%
CATALYST STYLE: 21